Ruby – The Birthstone of July – Part 4

Synthetic and imitation rubies

In 1837, Gaudin made the first synthetic rubies by fusing potash alum at a high temperature with a little chromium as a pigment. In 1847, Ebelmen made white sapphire by fusing alumina in boric acid. In 1877, Frenic and Freil made crystal corundum from which small stones could be cut. Frimy and Auguste Verneuil manufactured artificial ruby by fusing BaF2 and Al2O3 with a little chromium at red heat. In 1903, Verneuil announced he could produce synthetic rubies on a commercial scale using this flame fusion process. By 1910, Verneuil’s laboratory had expanded into a 30 furnace production facility, with annual gemstone production having reached 1,000 kilograms (2,000 lb) in 1907.

Other processes in which synthetic rubies can be produced are through Czochralski’s pulling process, flux process, and the hydrothermal process. Most synthetic rubies originate from flame fusion, due to the low costs involved. Synthetic rubies may have no imperfections visible to the naked eye but magnification may reveal curves, striae and gas bubbles. The fewer the number and the less obvious the imperfections, the more valuable the ruby is; unless there are no imperfections (i.e., a perfect ruby), in which case it will be suspected of being artificial. Dopants are added to some manufactured rubies so they can be identified as synthetic, but most need gemological testing to determine their origin.

Synthetic rubies have technological uses as well as gemological ones. Rods of synthetic ruby are used to make ruby lasers and masers. The first working laser was made by Theodore H. Maiman in 1960.  Maiman used a solid-state light-pumped synthetic ruby to produce red laser light at a wavelength of 694 nanometers (nm). Ruby lasers are still in use. Rubies are also used in applications where high hardness is required such as at wear exposed locations in modern mechanical clockworks, or as scanning probe tips in a coordinate measuring machine.

Imitation rubies are also marketed. Red spinels, red garnets, and colored glass have been falsely claimed to be rubies. Imitations go back to Roman times and already in the 17th century techniques were developed to color foil red—by burning scarlet wool in the bottom part of the furnace—which was then placed under the imitation stone. Trade terms such as balas ruby for red spinel and rubellite for red tourmaline can mislead unsuspecting buyers. Such terms are therefore discouraged from use by many gemological associations such as the Laboratory Manual Harmonisation Committee (LMHC).

Records and famous rubies

Rubies at the National Museum of Natural History, Washington, D.C., USA

  • The Smithsonian’s National Museum of Natural History in Washington, D.C. has some of the world’s largest and finest ruby gemstones. The 23.1 carats (4.62 g) Burmese ruby, set in a platinum ring with diamonds, was donated by businessman and philanthropist Peter Buck in memory of his late wife Carmen Lúcia. This gemstone displays a richly saturated red color combined with an exceptional transparency. The finely proportioned cut provides vivid red reflections. The stone was mined from the Mogok region of Burma (now Myanmar) in the 1930s.
  • In 2007 the London jeweler Garrard & Co featured on their website a heart-shaped 40.63-carat ruby.
  • On December 13/14, 2011 Elizabeth Taylor’s complete jewellery collection was auctioned by Christie’s. Several ruby-set pieces were included in the sale, notably a ring set with an 8.24 ct gem that broke the ‘price-per-carat’ record for rubies ($512,925 per carat, i.e. over $4.2 million in total), and a necklace that sold for over $3.7 million.
  • The Liberty Bell Ruby is the largest mined ruby in the world. It was stolen in a heist in 2011.
  • The Sunrise Ruby is the world’s most expensive ruby, most expensive colored gemstone, and most expensive gemstone other than a diamond. In May 2015, it sold at auction in Switzerland to an anonymous buyer for US$30 million.
  • A synthetic ruby crystal became the gain medium in the world’s first optical laser, conceived, designed and constructed by Theodore H. “Ted” Maiman, on the 16th of May, 1961 at Hughes Research Laboratories. The concept of electromagnetic radiation amplification through the mechanism of stimulated emission had already been successfully demonstrated in the laboratory by way of the Maser, using other materials such as ammonia and, later, ruby, but the ruby laser was the first device to work at optical (694.3 nm) wavelengths. Maiman’s prototype laser is still in working order.

Historical and cultural references

  • An early recorded transport and trading of rubies arises in the literature on the North Silk Road of China, wherein about 200 BC rubies were carried along this ancient track way moving westward from China.
  • Rubies have always been held in high esteem in Asian countries. They were used to ornament armor, scabbards, and harnesses of noblemen in India and China. Rubies were laid beneath the foundation of buildings to secure good fortune to the structure.

(Information from Wikipedia, the free encyclopedia)

Ruby – The Birthstone of July – Part 3

Treatments and enhancements

Corundum-winza-17d.jpg
Natural ruby crystals from WinzaTanzania

Improving the quality of gemstones by treating them is common practice. Some treatments are used in almost all cases and are therefore considered acceptable. During the late 1990s, a large supply of low-cost materials caused a sudden surge in supply of heat-treated rubies, leading to a downward pressure on ruby prices.

Improvements used include color alteration, improving transparency by dissolving rutile inclusions, healing of fractures (cracks) or even completely filling them.

The most common treatment is the application of heat. Most rubies at the lower end of the market are heat treated to improve color, remove purple tinge, blue patches, and silk. These heat treatments typically occur around temperatures of 1800 °C (3300 °F). Some rubies undergo a process of low tube heat, when the stone is heated over charcoal of a temperature of about 1300 °C (2400 °F) for 20 to 30 minutes. The silk is partially broken, and the color is improved.

Another treatment, which has become more frequent in recent years, is lead glass filling. Filling the fractures inside the ruby with lead glass (or a similar material) dramatically improves the transparency of the stone, making previously unsuitable rubies fit for applications in jewelry. The process is done in four steps:

  1. The rough stones are pre-polished to eradicate all surface impurities that may affect the process.
  2. The rough is cleaned with hydrogen fluoride.
  3. The first heating process during which no fillers are added. The heating process eradicates impurities inside the fractures. Although this can be done at temperatures up to 1400 °C (2500 °F) it most likely occurs at a temperature of around 900 °C (1600 °F) since the rutile silk is still intact.
  4. The second heating process in an electrical oven with different chemical additives. Different solutions and mixes have shown to be successful, however mostly lead-containing glass-powder is used at present. The ruby is dipped into oils, then covered with powder, embedded on a tile and placed in the oven where it is heated at around 900 °C (1600 °F) for one hour in an oxidizing atmosphere. The orange colored powder transforms upon heating into a transparent to yellow-colored paste, which fills all fractures. After cooling the color of the paste is fully transparent and dramatically improves the overall transparency of the ruby.

If a color needs to be added, the glass powder can be “enhanced” with copper or other metal oxides as well as elements such as sodium, calcium, potassium etc.

The second heating process can be repeated three to four times, even applying different mixtures. When jewelry containing rubies is heated (for repairs) it should not be coated with boracic acid or any other substance, as this can etch the surface; it does not have to be “protected” like a diamond.

The treatment can identified by noting bubbles in cavities and fractures using a 10x loupe.

More about this beautiful gemstone, the birthstone of July – Ruby in Part 4.

(Information from Wikipedia, the free encyclopedia)

Ruby – The Birthstone of July – Part 2

Ruby vs. pink sapphire

Generally, gemstone-quality corundum in all shades of red, including pink, are called rubies. However, in the United States, a minimum color saturation must be met to be called a ruby; otherwise, the stone will be called a pink sapphire. Drawing a distinction between rubies and pink sapphires is relatively new, having arisen sometime in the 20th century. Often, the distinction between ruby and pink sapphire is not clear and can be debated. As a result of the difficulty and subjectiveness of such distinctions, trade organizations such as the International Colored Gemstone Association (ICGA) have adopted the broader definition for ruby which encompasses its lighter shades, including pink.

Occurrence and mining

Historically, rubies have also been mined in Thailand, in the Pailin and Samlout District of Cambodia, as well as in Afghanistan, Australia, Brazil, Colombia, India, Namibia, Japan, and Scotland; after the Second World War ruby deposits were found in Madagascar, Nepal, Pakistan, Tajikistan, Tanzania, and Vietnam.

The Republic of Macedonia is the only country in mainland Europe to have naturally occurring rubies. They can mainly be found around the city of Prilep. Macedonian rubies have a unique raspberry color. The ruby is also included on the Macedonian coat of arms. A few rubies have been found in the U.S. states of Montana, North Carolina, South Carolina and Wyoming.

Spinel, another red gemstone, is sometimes found along with rubies in the same gem gravel or marble. Red spinels may be mistaken for rubies by those lacking experience with gems. However, the finest red spinels can have values approaching that of an average ruby.

South Asia

The Mogok Valley in Upper Myanmar (Burma) was for centuries the world’s main source for rubies. That region has produced some exceptional rubies, however in recent years few good rubies have been found. In central Myanmar, the area of Mong Hsu began producing rubies during the 1990s and rapidly became the world’s main ruby mining area. The most recently found ruby deposit in Myanmar is in Namya (Namyazeik) located in the northern state of Kachin.

Rubies are also mined in Afghanistan and Pakistan. In Pakistani Kashmir there are vast proven reserves of millions of rubies, worth up to half a billion dollars. However, as of 2017 there was only one mine (at Chitta Katha) due to lack of investment. In Afghanistan, rubies are mined at Jegdalek.

In Sri Lanka, lighter shades of rubies (often “pink sapphires”) are more commonly found.

Factors affecting value

Rubies, as with other gemstones, are graded using criteria known as the four Cs, namely color, cut, clarity and carat weight. Rubies are also evaluated on the basis of their geographic origin.

Color: In the evaluation of colored gemstones, color is the most important factor. Color divides into three components: huesaturation and tone. Hue refers to color as we normally use the term. Transparent gemstones occur in the pure spectral hues of red, orange, yellow, green, blue, violet. In nature, there are rarely pure hues, so when speaking of the hue of a gemstone, we speak of primary and secondary and sometimes tertiary hues. Ruby is defined to be red. All other hues of the gem species corundum are called sapphire. Ruby may exhibit a range of secondary hues, including orange, purple, violet, and pink.

Stay tuned for Part 3 about Rubies, the July Birthstone!

(Information from Wikipedia, the free encyclopedia)

Ruby – The Birthstone of July

ruby is a pink to blood-red colored gemstone, a variety of the mineral corundum (aluminium oxide). Other varieties of gem-quality corundum are called sapphires. Ruby is one of the traditional cardinal gems, together with amethyst, sapphire, emerald, and diamond. The word ruby comes from ruber, Latin for red. The color of a ruby is due to the element chromium.

Some gemstones that are popularly or historically called rubies, such as the Black Prince’s Ruby in the British Imperial State Crown, are actually spinels. These were once known as “Balas rubies”.

The quality of a ruby is determined by its color, cut, and clarity, which, along with carat weight, affect its value. The brightest and most valuable shade of red called blood-red or pigeon blood, commands a large premium over other rubies of similar quality. After color follows clarity: similar to diamonds, a clear stone will command a premium, but a ruby without any needle-like rutile inclusions may indicate that the stone has been treated. Ruby is the traditional birthstone for July and is usually pinker than garnet, although some rhodolite garnets have a similar pinkish hue to most rubies. The world’s most valuable ruby is the Sunrise Ruby.

All natural rubies have imperfections in them, including color impurities and inclusions of rutile needles known as “silk”. Gemologists use these needle inclusions found in natural rubies to distinguish them from synthetics, simulants, or substitutes. Usually, the rough stone is heated before cutting. These days, almost all rubies are treated in some form, with heat treatment being the most common practice. Untreated rubies of high quality command a large premium.

Some rubies show a three-point or six-point asterism or “star”. These rubies are cut into cabochons to display the effect properly. Asterisms are best visible with a single-light source and move across the stone as the light moves or the stone is rotated. Such effects occur when light is reflected off the “silk” (the structurally oriented rutile needle inclusions) in a certain way. This is one example where inclusions increase the value of a gemstone. Furthermore, rubies can show color changes—though this occurs very rarely—as well as chatoyancy or the “cat’s eye” effect.

More about these beautiful gemstones in Part 2 about Rubies!

(Information from Wikipedia, the free encyclopedia)